Induksi Brazing Parts Steel kanggo Plate Carbide Tungsten

Induksi Brazing Parts Steel kanggo Plate Carbide Tungsten

adil
Induksi Brazing of Steel Steel menyang Plate Carbide Tungsten

Wear

DW-UHF-6KW-III mesin kurang empuk genggol

Perangan baja baja induksi

test 1

Bahan
• Rod baja: 19.05 mm (0.75 ″) OD, 82.55 mm (3.25 ″) Panjang

• Pelat Karbida Tungsten: 38.1 mm (1.5 ″) OD, 10.16 mm (0.4 ″) Kandel

• Paduan: 19.05 mm (0.75 ″) Cakram gir

Power: 4.0 kW
Suhu: Kira-kira 760 ° C (1400 ° F)
wektu: 40 detik

test 2

Bahan
• Rod baja: 12.7 mm (0.50 ″) OD, 76.2 mm (3 ″) Panjang

• Pelat Karbida Tungsten: 19.05 mm (0.75 ″) OD, 6.35 mm (0.25 ″) Kandel

• Paduan: 12.7 mm (0.50 ″) Cakram gir

Power: 2.36 kW
Suhu: Kira-kira 760 ° C (1400 ° F)
wektu: 23 detik

test 3

Bahan
• Rod baja: 12.7 mm (0.50 ″) OD, 76.2 mm (3 ″) Panjang

• Pelat Karbida Tungsten: 1 ″ OD, 1.39mm (0.055 ″) Kandel

• Paduan: 12.7 mm (0.50 ″) Cakram gir

Power: 2.36 kW
Suhu: Kira-kira 760 ° C (1400 ° F)
wektu: 20-25 sec (Pulsing urip / mati)

test 4

Bahan
• Rod baja: 6.35 mm (0.25 ″) OD, 76.2 mm (3 ″) Panjang

• Tungsten Carbide Plate: 21.08mm (0.83 ″) OD, 1.65mm (0.065 ″) kekandelan

• Paduan: 6.35 mm (0.25 ″) Cakram gir

Power: 1.96 kW
Suhu: Kira-kira 760 ° C (1400 ° F)Induksi karbida baja karbidaPerangan baja baja induksiPerangan baja baja induksi
wektu: 20 sec (Pulsing ing / mati)

Hasil lan Kesimpulan:

Babagan baja sing beda kanggo disk karbida bisa nganggo gulungan induksi siji. Kekuwatan diatur kanthi mateni lan mateni nggunakake saklar kanggo nyegah panas saka karbida.

 

=

=